概述
Aluminum Alloy Alclad 2024(UNS A92024) Sheet is a aluminum alloy sheet/plate. Relevant grade or standard references include UNS (USA) A92024 (core) / A82024 (Alclad); AA / ASTM (USA) 2024 / Alclad 2024; AMS 4040 (Alclad T3), 4041 (Alclad T42), 4475 (Alclad T4 coil); EN / ISO (Europe) EN AW-2024 (AlCu4Mg1) / EN AW-2024 clad; DIN (Germany) 3.1355 (AlCu4MgSi) — approximate. Typical applications include Aerospace; Military / Defense — armor plate, missile components; Transportation — truck wheels, structural parts; Automotive — high-stress structural components. Available size information includes Thickness:0.2 – 6.35 mm (0.008" – 0.250"); Width:500 – 2,500 mm (20" – 98"); Length:1,000 – 6,000 mm (40" – 240").
描述（英文）
Alclad 2024 (UNS A82024) sheet is the quintessential aerospace aluminum alloy, combining the high strength, excellent fatigue resistance, and good fracture toughness of 2024 aluminum with dramatically improved corrosion resistance through a metallurgically bonded high-purity aluminum cladding layer. Available primarily in O, T3, and T4 tempers with thicknesses from 0.2–6.35 mm, it is the material of choice for aircraft fuselage skins, wing skins, and structural panels where high strength-to-weight ratio and reliable performance under cyclic loading are paramount. The Alclad layer provides sacrificial corrosion protection, making it far more durable in service than bare 2024.
尺寸范围
- Thickness:0.2 – 6.35 mm (0.008" – 0.250")
- Width:500 – 2,500 mm (20" – 98")
- Length:1,000 – 6,000 mm (40" – 240")
牌号标准
| 标准体系 | 数值 |
|---|---|
| UNS (USA) | A92024 (core) / A82024 (Alclad) |
| AA / ASTM (USA) | 2024 / Alclad 2024 |
| 🇺🇸 AMS | 4040 (Alclad T3), 4041 (Alclad T42), 4475 (Alclad T4 coil) |
| EN / ISO (Europe) | EN AW-2024 (AlCu4Mg1) / EN AW-2024 clad |
| DIN (Germany) | 3.1355 (AlCu4MgSi) — approximate |
| JIS (Japan) | A2024 (A2024P / A2024S) |
| GB (China) | 2A12 (LY12) — closest domestic equivalent |
| GOST (Russia) | D16 / D16T |
化学成分
| 元素 | 数值 |
|---|---|
| Core | 2024 |
| Al | bal |
| Cu | 4.5 |
| Mn | 0.6 |
| Mg | 1.5 |
| Caldding | Al:99.3min |
机械性能
| productCenter.property | 数值 |
|---|---|
| O (Annealed)Tensile Strength (MPa) min | 205 |
| O (Annealed)Yield Strength (MPa) min | 95 |
| O (Annealed)Elongation (%) min | 10–12 |
| T3 (Solution HT + cold work + natural aged)Tensile Strength (MPa) min | 440 – 485 |
| T3 (Solution HT + cold work + natural aged)Yield Strength (MPa) min | 325 – 360 |
| T3 (Solution HT + cold work + natural aged)Elongation (%) min | 12 – 15 |
| T4 (Solution HT + naturally aged)Tensile Strength (MPa) min | 400 – 440 |
| T4 (Solution HT + naturally aged)Yield Strength (MPa) min | 248 – 275 |
| T4 (Solution HT + naturally aged)Elongation (%) min | 15 – 18 |
| T62 (Solution HT + artificially aged)Tensile Strength (MPa) min | 450 – 490 |
| T62 (Solution HT + artificially aged)Yield Strength (MPa) min | 395 – 420 |
| T62 (Solution HT + artificially aged)Elongation (%) min | 5 – 8 |
物理性能
| 性能 | 单位 | 数值 |
|---|---|---|
| Density (core) | g/cm³ | 2.78 g/cm³ (0.100 lb/in³) |
| Density (Alclad overall) | g/cm³ | 2.75 – 2.77 g/cm³ |
应用场景
- Aerospace
- Military / Defense — armor plate, missile components
- Transportation — truck wheels, structural parts
- Automotive — high-stress structural components
- Sporting Goods — bicycle frames, lacrosse sticks
- Industrial — structural components, tooling, fixtures
- Research / Prototyping — aerospace-grade test specimens