Обзор
HASTELLOY Alloy 6 (UNS N06007) is a nickel-chromium-molybdenum superalloy containing Ni bal, Cr 22, Fe 19.5, Mo 6.5, and Cb+Ta 2, designed for excellent resistance to both oxidizing and reducing chemical environments. The high iron and chromium content combined with molybdenum additions provides versatile corrosion resistance across a wide range of acid and alkaline media, while the niobium (columbium) and tantalum additions enhance resistance to intergranular corrosion. The alloy is widely used in chemical process equipment, particularly for handling sulfuric acid, phosphoric acid, and mixed acid solutions
Описание (Английский)
HASTELLOY Alloy 6 is supplied in the sheet solution heat-treated condition, delivering yield strength of 317 MPa, tensile strength of 703 MPa, elongation of 62%, and hardness of HRB 84. The alloy is manufactured to multiple ASTM standards covering sheet/plate/strip (B 582), rod (B 581), pipe and tube (B 619, B 622, B 626), and fittings (B 366). The exceptional ductility (62%) provides outstanding formability for complex fabrications. HASTELLOY 6 is widely used in chemical processing, pulp and paper production, and flue gas desulfurization systems where balanced corrosion resistance and good fabricability are required.
Диапазон Размеров
- Sheet: 0.5 - 6 mm thickness, Width up to 1200 mm, Length up to 3000 mm
- Plate: 6 - 50 mm thickness, Width up to 1500 mm, Length up to 3000 mm
- Strip: 0.1 - 3 mm thickness, Width up to 300 mm, Coil
Спецификация Марки
| Система | Значение |
|---|---|
| 🇺🇸 ASTM | B 582 |
| European | EN 10095, DIN 17750 |
| China | GB/T 15007, GB/T 2054 |
| Japan | JIS H4551 |
| Aerospace (limited) | AMS |
Химический Состав
| Элемент | Значение |
|---|---|
| Ni | Bal |
| Cr | 22 |
| Fe | 19.5 |
| Mo | 6.5 |
| Cb+Ta | 2 |
| Co | 2.5 max |
| Mn | 1.5 |
| Si | 1 max |
| W | 1 max |
| C | 0.05 max |
Механические Свойства
| productCenter.property | Значение |
|---|---|
| Yield Strength (0.2% offset) | 317 MPa |
| Tensile Strength | 703 MPa |
| Elongation (in 2 in) | 62% |
| Hardness | HRB 84 |
Физические Свойства
| Свойство | Единица | Значение |
|---|---|---|
| Density | g/cm³ | 0.316 lb/cu in |
| Specific Gravity | - | 8.75 |
| Melting Point | °C | 2470 °F |
| Specific Heat (32-212°F) | J/kg·K | 0.105 Btu/lb/°F |
| Thermal Expansion Coefficient (32-212°F) | ×10⁻⁶/K | 6.8 in/in/°F × 10⁻⁶ |
| Thermal Conductivity (32-212°F) | W/m·K | 76 Btu/sq ft/hr/°F/in |
| Electrical Resistivity (68°F) | μΩ·cm | 696 ohms/cir mil ft |
| Tensile Modulus of Elasticity | GPa | 30.2 × 10⁶ psi |
Применение
- - Chemical process industry equipment
- - Sulfuric acid production equipment
- - Phosphoric acid handling systems
- - Pulp and paper production
- - Flue gas desulfurization (FGD) systems
- - Mixed acid solution processing
- - Heat exchangers and reactors