Алюминиевый СплавЛист/Плита
Обзор
1060 aluminum is a commercially pure wrought aluminum with a minimum aluminum content of 99.6%. It is one of the higher-purity grades in the 1000-series. The H14 temper designates strain-hardened to approximately 1/2 hard condition, providing a good balance of moderate strength and retained formability.
Описание (Английский)
1060 aluminum is a commercially pure wrought aluminum with a minimum aluminum content of 99.6%. It is one of the higher-purity grades in the 1000-series. The H14 temper designates strain-hardened to approximately 1/2 hard condition, providing a good balance of moderate strength and retained formability.
Диапазон Размеров
- Thickness:0.2 mm – 6.35 mm (0.008" – 0.250")
- Width:500 mm – 2,000 mm (20" – 80")
- Length:1,000 mm – 4,000 mm (40" – 157")
- Common Stock Sizes:1,000 × 2,000 mm · 1,220 × 2,440 mm (4' × 8') · 1,250 × 2,500 mm · 1,500 × 3,000 mm
- Coil / Slit Sheet:Available slit to width
Спецификация Марки
| Система | Значение |
|---|---|
| 🇺🇸 UNS | A91060 |
| AA | 1060 |
| EN / ISO | EN AW-1060 (Al99.6) |
| 🇩🇪 DIN | 3.0255 (Al99.6) |
| 🇯🇵 JIS | A1060 (A1060P-H14 for sheet) |
| 🇨🇳 GB | 1060 (GB/T 3880) |
| NF | A5 |
Химический Состав
| Элемент | Значение |
|---|---|
| Al | ≥ 99.60 |
| Si | ≤ 0.25 |
| Fe | ≤ 0.35 |
| Cu | ≤ 0.05 |
| Mn | ≤ 0.03 |
| Mg | ≤ 0.03 |
| Zn | ≤ 0.05 |
| V | ≤ 0.05 |
| Ti | ≤ 0.03 |
| Other (each) | ≤ 0.03 |
Механические Свойства
| productCenter.property | Значение |
|---|---|
| Tensile Strength Rm | 105 – 135 MPa |
| 0.2% Yield Strength | 85 – 115 MPa |
| Elongation A (50 mm) | 6 – 12% |
| Shear Strength | ~75 MPa |
| Hardness | 28 – 35 HB |
| Fatigue Strength (10⁸ cycles) | ~50 MPa |
Физические Свойства
| Свойство | Единица | Значение |
|---|---|---|
| Density | g/cm³ | 2.70 g/cm³ (0.098 lb/in³) |
| Melting Point Range | °C | 646 – 657 °C (1,195 – 1,215 °F) |
| Modulus of Elasticity | GPa | 69 GPa (10 × 10⁶ psi) |
| Shear Modulus | - | 26 GPa |
| Poisson's Ratio | - | 0.33 |
| Thermal Conductivity (20°C) | W/m·K | 234 W/(m·K) |
| Electrical Conductivity | - | ~62% IACS (annealed); ~61% IACS (H14) |
| Electrical Resistivity (20°C) | μΩ·cm | ~2.78 μΩ·cm |
| CTE (20–100°C) | - | 23.6 ppm/°C (13.1 ppm/°F) |
| Specific Heat (20°C) | J/kg·K | 0.90 J/(g·K) |
| Magnetism | - | Non-magnetic |
Применение
- Electrical
- Heat Transfer
- Electronics
- Lighting
- Architecture
- Packaging
- Insulation
- Signage
- Chemical
- General Fabrication