Baja KarbonLembaran/Pelat
Ringkasan
bozhong steel
Komposisi Kimia
| Elemen | Min | Maks | Nilai |
|---|---|---|---|
| C | - | - | 0.12-0.24% |
| Mn | - | - | 0.70-1.60% |
| Si | - | - | 0.20-0.70% |
| Cr | - | - | 0.20-1.20% |
| Ni | - | - | 0.20-1.50% |
| Mo | - | - | 0.10-0.60% |
Sifat Mekanis
| productCenter.property | Nilai |
|---|---|
| Hardness in annealed condition (HB) | 250 HB maxi |
| Hardness in heat treated condition (HRC) | 56 |
| Young modulus (GPA) | 205 |
| Compression strength MPA (ksi) | 2210 (320) |
| KV*J (ft.lbs) | 40 (29.5) |
| Hardness in annealed condition (HB) | 62 |
| Hardness in heat treated condition (HRC) | 205 |
| Young modulus (GPA) | 2550 (370) |
| Compression strength MPA (ksi) | 25 (18.4) |