Copper AlloySheet/Plate
Description (English)
C11000 (Electrolytic Tough Pitch Copper) mechanical properties vary significantly based on temper (cold-work condition). As a pure copper, it is relatively soft and ductile in the annealed state but can be significantly strengthened through cold working.
Size Range
- Sheet: Thickness:0.2 mm β 6.35 mm (0.008" β 0.25");Width:300 mm β 1,220 mm (12" β 48");Length:1,200 mm β 3,660 mm (4' β 12')
- Plate:thickness:6.35 mm β 50 mm (0.25" β 2") β and up to 100 mm+ on request;Width:300 mm β 1,000 mm (12" β 40") standard; wider on custom order;Length:1,200 mm β 3,000 mm (4' β 10') standard; cut-to-length available
Grade Specification
| System | Value |
|---|---|
| πΊπΈ UNS | C11000 |
| πΊπΈ ASTM | B152 |
| EN / DIN | 2.0065 Β· E-Cu58 |
| π―π΅ JIS | C1100 |
| GB/T | T2 (GB/T 5231) |
| SAE | CA110 |
Chemical Composition
| Element | Value |
|---|---|
| C | 99.90min |
Physical Properties
| Property | Unit | Value |
|---|---|---|
| Annealed (O60)Tensile Strength (MPa) | - | 180β260Mpa |
| Annealed (O60)Yield Strength (MPa) | - | 70Mpa |
| Annealed (O60)Elongation in 51mm (%) | - | 35 |
| 1/8 Hard (H00)Tensile Strength (MPa) | - | 220β275Mpa |
| 1/8 Hard (H00)Yield Strength (MPa) | - | β |
| 1/8 Hard (H00)Elongation in 51mm (%) | - | - |
| 1/4 Hard (H01)Tensile Strength (MPa) | - | 235β290Mpa |
| 1/4 Hard (H01)Yield Strength (MPa) | - | 220Mpa |
| 1/4 Hard (H01)Elongation in 51mm (%) | - | 23 |
| 1/2 Hard (H02)Tensile Strength (MPa) | - | 255β315Mpa |
| 1/2 Hard (H02)Yield Strength (MPa) | - | 255Mpa |
| 1/2 Hard (H02)Yield Strength (MPa) | - | 255Mpa |
| 1/2 Hard (H02)Elongation in 51mm (%) | - | 20 |
Applications
- Electrical & Electronics
- Thermal / Heat Transfer
- Architecture & Building
- Industrial & General